Modelling of the High-Energy Ball Milling Process
Experimental. Elementary Ti (<40 μm, 99.9%) and C (5 μm, 99.9%) powder mixture was sealed into a stainless-steel vial with 5 stainless-steel balls (15 mm in diameter) in a glove box filled with purified argon to avoid oxidation. The ball to powder weight ratio was 70:1. The milling process was performed at room temperature using a high-energy ...